| Grades | TP series - 201, 304, 304H, 304L, 304N, 304LN, 309, 310, 310S, 316, 316H, 316L, 316LN, 316Ti, 317, 317L, 321, 321H, 347, 347H, 904L. UNS series - S31803, S32750, S32760, NO8904. |
| Specifications | ASTM A249, A269, A270 |
| Size | 1/8” NB to 24” NB, 1/4” OD to 24” OD sizes stainless steel welded tubes also available |
| Outer Diameter | 1/4" to 6" (6.35-165.2mm) |
| Wall Thickness | 0.4mm upto client requirement |
| Length | Up to 6 meters, custom cut lengths |
| Type | Seamless, Welded, Bright Annealed, Mechanically Polished, Electropolished, Semi Welded |
| Finish | BA Finish inside and outside, Electropolished finish inside and outside |
Specification
| Sheet/Plate | Round Bar | Pipe | Tube | Fittings | Forgings |
| QQ N 281 | ASME SB-164 |
|
|
| QQ N 281 |
Chemical Composition
| C | MN | P | S | Si | Cr | Ni | Mo | Cu | Co | Cb+Ta | Ti | Al | Fe | Other |
| .3 max | 2.0 max |
| .025-.060 | .5 max |
| 63.0 min |
| 28 - 34 |
|
|
|
| 2.5 max |
|
Mechanical & Physical Properties
| Density | Melting Point | Tensile Strength | Yield Strength (0.2%Offset) | Elongation |
| 8.44 g/cm3 | 1350 °C (2460 °F) | Psi – 1,60,000 , MPa – 1100 | Psi – 1,15,000 , MPa – 790 | 20 % |
Monel R405 is the free machining version of Monel 400. It is a nickel-copper alloy with a controlled amount of sulfur added to provide sulfide inclusions that act as chip breakers during machining. Like Monel 400, alloy R-405 is resistant to sea water and steam at high temperatures as well as to salt and caustic solutions. Monel R405 is a solid solution alloy that can only be hardened by cold working. This nickel alloy exhibits characteristics like good corrosion-resistance, good weldability and high strength. A low corrosion rate in rapidly flowing brackish or seawater combined with excellent resistance to stress corrosion cracking in most freshwaters, and its resistance to a variety of corrosive conditions led to its wide use in marine applications and other non-oxidizing chloride solutions. This nickel steel alloy is particularly resistant to hydrochloric and hydrofluoric acidswhenthey are de-aerated. As would be expected from its high copper content, alloy R-405 is rapidly attacked by nitric acid and ammonia systems.
As with alloy 400, Monel R-405 is virtually immune to chloride ion stress corrosion cracking in typical environments. Generally, its corrosion resistance is very good in reducing environments, but poor in oxidizing conditions. It is not useful in oxidizing acids, such as nitric acid and nitrous. Nevertheless, it is resistant to most alkalis, salts, waters, food products, organic substances and atmospheric conditions at normal and elevated temperatures.